White Marble Laminate
Leveraging on our years of experience, we are indulged in manufacturing and supplying premium quality White Marble Laminate. These laminated are designed in strict conformance with international standards, under the closed supervision of experienced professionals. Owing to their smooth texture, alluring look, high resistance to chemicals & temperature and durability, our marble laminates are highly appreciated in the market. We offer White Marble Laminate at very reasonable rates to our customers.
Products
Super Hylam (P) Limited Manufactures Switch Board In 2.0 Mm, 2.5, 3.0 Mm & 4.0 Mm Thickness. (Other Thickness May Be Available On Request ) Sheet Size Is 2440x1220 Mm Or 1220x1220 Mm.
Finish
Available In High Gloss & Matt Finish.
Tested
All Test Methods Are Carried Out Under Bureau Of Indian Standards.
Application
Super Hylam Switch Board Can Be Easily Cut And Drilled To Make It Convenient For Use In Paneling Of Switch Board For Office & Home.
Care And Maintenance
Wipe Clean With Ordinary Soap Or Household Ammoniated Liquid Detergent. For Stubborn Stains Use Diluted Organic Solvents Or Stain Remover.
High Pressure Decorative Laminated Sheet
| SO. NO | PROPERTIES | UNIT | SPECIFIED VALUE
AS PER IS:2046/95 | TYPICAL VALUE |
| 1. | THICKNESS |
| 2.0 ± 0.15 | 2.05 |
|
|
| MM | 2.5 ± 0.18 | 2.55 |
|
|
|
| 3.0 ± 0.20 | 3.05 |
| 2. | RESISTANCE TO IMMERSION IN BOILING WATER |
|
|
|
|
| (A) INCREASE IN WEIGHT | % | 3.75 (MAX.) | 2.05 |
|
| (B) INCREASE IN THICKNESS | % | 4.0 (MAX.) | 2.35 |
|
| (C) APPEARANCE | GRADE | NOT WORSE THAN 4 | 5 |
| 3. | RESISTANCE TO DRY HEAT 180
| GRADE | NOT WORSE THAN 4 | 5 |
| 4. | RESISTANCE TO CRAZING | GRADE | NOT WORSE THAN 4 | COMPLIES |
| 5. | RESISTANCE TO SURFACE WEAR | REV. | 350 (MIN) | 410 |
| 6. | RESISTANCE TO STAINING |
|
|
|
|
| (A) COFFEE | GRADE | NOT WORSE THAN 5 | COMPLIES |
|
| (B) SHOE POLISH | GRADE | NOT WORSE THAN 5 | COMPLIES |
|
| (C) CITRIC ACID (10% SOLUTION) | GRADE | NOT WORSE THAN 5 | COMPLIES |
|
| (D) ACETONE | GRADE | NOT WORSE THAN 5 | COMPLIES |
|
| (E) SODIUM HYDROXIDE (25% SOLUTION) | GRADE | NOT WORSE THAN 5 | COMPLIES |
|
| (F) HYDROGEN PEROXIDE (30% SOLUTION) | GRADE | NOT WORSE THAN 5 | COMPLIES |
| 7. | DIMENSIONAL STABILITY AT L | % | 0.30 (MAX.) | 0.20 |
|
| DEVIATED STABILITY T | % | 0.65 (MAX.) | 0.30 |
| 8. | DIMENSIONAL STABILITY L | % | 0.20 (MAX.) | 0.10 |
|
| AT 20 C | % | 0.30 (MAX.) | 0.15 |
| 9. | FLEXURAL MODULUS | MPA | 10,000 (MIN.) | 12500 |
| 10. | FLEXURAL STRENGTH | MPA | 100 (MIN.) | 110 |
| 11. | TENSILE STRENGTH | MPA | 70 (MIN.) | 85 |
| 12. | RESISTANCE TO CIGARETTE BURN | GRADE | NOT WORSE THAN 3 | COMPLIES |
| 13. | RESISTANCE TO STEAM | GRADE | NOT WORSE THAN 4 | COMPLIES |
| 14. | RESISTANCE TO MOISTURE | GRADE | NOT WORSE THAN 4 | COMPLIES |
| 15. | RESISTANCE TO SCRATCHING | N (MIN)) | 2.0 (MIN) | 3.5 |
| 16. | RESISTANCE TO COLOUR CHANGE |
|
|
|
|
| (A) IN XENON ARC LIGHT | GRADE | NOT WORSE THAN 6 | COMPLIES |
|
| (B) IN ENCLOSED CARBON ARC LIGHT | GRADE | NOT WORSE THAN 5 | COMPLIES |
| 17. | RESISTANCE TO IMPACT BY LARGE | MM. | 10 (MM) | NO DAMAGE |
|
| DIAMETER BALLS | (MAX.) |
|
|